By Thanakom Wirunmongkol, Narongchai O-Charoen

Year 2013

Abstract

Zinc oxide powders with different morphology have been successfully prepared by adopting zinc nitrate hexahydrate (Zn(NO[subscript3]) [subscript2].6H[subscript2]O) and sodium hydroxide (NaOH) as the starting precursors in the mole ratio of Zn(NO[subscript2]-6H[subscript2]O : NaOH of 1:2 and 1:10, via the simple hydrothermal process (60 degree Celsius for 611.) using Thai autoclave unit. The shape, size, and crystalline structures of the as-prepared ZnO powders were characterized by scanning electron microscope (SEM), transmission electron microscope (TEM) and x-ray diffraction (XRD). At the lower alkaline concentration, the prepared showed powder short prism-like shape with hexagonal phase. The average particle size was about 0.3-0.5 (mu)m in width and 0.5-0.7 (mu)m in length. At the higher alkaline concentration, the microstructure of ZnO powders change in turn from short prism to flower-like shapes. The particle size was about 30-80 nm in width and 0.5-1 (mu)m in length. This preparation method provide a simple hydrothermal routes to fabricate ZnO powders using Thai autoclave Unit.

Download : Simple Hydrothennal Preparation of Zinc Oxide Powders Using Thai Autoclave Unit